| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 300 - 360 |
| Density (23°C) | g mL-1 | 1.27 - 1.29 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 2.30 - 2.65 |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | 139 - 175 |
| Thermal Conductivity | W / mK | |
| Rockwell Hardness, M Scale | n/a | |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 88 - 112 |
| Tensile Strength, Break at 23 C | MPa | 70 - 105 |
| Elongation, Yield | % | 5.2 - 5.4 |
| Elongation, Break | % | 20 - 100 |
| Tensile Modulus at 23 C | GPa | 2.9 - 3.8 |
| Flexural Strength, max | MPa | 128 - 168 |
| Flexural Modulus | GPa | 3.0 - 3.9 |
| Compressive Strength | MPa | |
| Charpy Notched | kJ / m2 | 4.0 - 5.5 |
| Charpy Unnotched | kJ / m2 | No Break, 22 - 62 |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | 1016 | |
| Dielectric Strength | V/mm x 104 | 8.4 | |
| Dielectric Constant @ 1 MHz | n/a | 2.5 - 2.6 | |
| Dissipation Factor @ 1 MHz | n/a |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 320 - 360 | |
| Mold Shrinkage | % | ||
| Continuous Service Temperature | °C | 255 | |
| Water Absorption, 24 hr. Immersion | % | 0.2 - 0.5 |